Quick Welds

[bruno8747]

Here are just some quick test welds I did at my job.

Machine: Miller 251
Gas: C-25 75% Argon/25% Co2
Wire Feed: 270
Voltage: 18.1

http://i5.photobucket.com/albums/y157/bruno8747/Meet/DSC02954Medium.jpg
http://i5.photobucket.com/albums/y157/bruno8747/Meet/DSC02955Medium.jpg
http://i5.photobucket.com/albums/y157/bruno8747/Meet/DSC02956Medium.jpg
http://i5.photobucket.com/albums/y157/bruno8747/Meet/DSC02957Medium.jpg
http://i5.photobucket.com/albums/y157/bruno8747/Meet/DSC02959Medium.jpg

[C91BLX7]

Damn, looks great.

[Fatman88]

Show off.....Now lets see what YOUR machine does!

[N9netwoAccord]

those look pretty damn good.

[benjerman112]

looks good nice job man

[flyinlow]

Nice looking beads.:tu:

[bruno8747]

Show off.....Now lets see what YOUR machine does!

I can weld like that with my little Lincoln but it depends on my mood.

And thanks for the comments. I am just doing Mig at work right now, I have to dip into aluminum one of these days. But other than that, Mild steel is fun to weld.

[Fatman88]

Have you finished your welding cart yet? I'm sure people would be interested in seeing that master piece.

[minoreparations]

welding is a very nice skill to have. what are you making?

i can honestly tell you that i wouldn't know where to start. it's something i would like to learn one day.

[bruno8747]

welding is a very nice skill to have. what are you making?

i can honestly tell you that i wouldn't know where to start. it's something i would like to learn one day.

That was just a piece that I made when I was bored. I use it to put in pens and stuff.

Its not too hard to start. Just have to practice. You get better with time.

[doughboy415]

Looks good man,slow down alittle and let it fill a little more,it wont be concave(low in the middle) and would tighten up the seams. Have you tried doing a circular or looping motion,I see you use the stop n go(back/forth) motion. I've been welding for 22yrs with certs in everything, I also gave the welding test(prehire and certs) where I used to work,:tu:

[bruno8747]

Looks good man,slow down alittle and let it fill a little more,it wont be concave(low in the middle) and would tighten up the seams. Have you tried doing a circular or looping motion,I see you use the stop n go(back/forth) motion. I've been welding for 22yrs with certs in everything, I also gave the welding test(prehire and certs) where I used to work,:tu:

Yea I normally weld a little better, But I just ran that through a little quick.

I do the circular motion mostly on other parts. Im not certified as yet, My job might send me to school to get my cets one of these days but I'm just hanging out and getting as much practice before going for the certs.

[scudweiser]

stack of dimes, i hate you. i cant do that with my AC220 stick machine :( . i want a bandsaw and a mig welder.

[d112crzy]

Doesn't look like it made that great of penetration. Also...clean up your surface and you won't get that splatter :p noob.

[bruno8747]

Doesn't look like it made that great of penetration. Also...clean up your surface and you won't get that splatter :p noob.

lol, Hey you keep on changing my oil and I'll keep on making good things.

I'll get some pics up of the real stuff that we make but I dont get the time.

[F22HB]

You should practice on some thin wall stuff.

[lokuputha]

those welds are clean! I first thought they were from a TIG. :tu:

[foamypirate]

Not bad at all! Oddly enough, I myself am better at stick welding than MIG, even though I've done WAY more MIG. I just have a knack for stick welding I guess.

[ikayto]

welds look nice.

[TheNextEpisode]

I specialize in jb welding, myself.




Good work, especially if that's a quick weld.